Comparative Evaluation of Microtensile Bond Strength in Three Different Dentin Luting Agents: An In vitro Study.

Aim: Long-term clinical success on indirect restorations is largely determined by bonding efficiency of the luting agent, with adhesion to dentin being the main challenge. Therefore, aim of this study was to assess the microtensile bond strength when using flowable resin composite, preheated resin composite and dual self-adhesive resin cement as dentin luting agents. Materials and Methods: Occlusal thirds of molar teeth were cut and randomly divided into 3 groups to be cemented: RelyX™U200, Filtek™ Z250 XT- preheated to 70° and Filtek Flow™ Z350XT. They were then thermocycled 5000 times between 5+/-2°C and 55+/-2°C. Subsequently, 10 microbars per group were prepared. The 30 samples were placed in saline solution for 24 hours at room temperature prior to microtensile test. This was performed with a digital universal testing machine at a crosshead speed of 0.5 mm/min. The bond strength values obtained were analyzed in Megapascals (MPa). Measures of central tendency such mean and measures of dispersion such standard deviation were used. In addition, the Kruskall Wallis non-parametric test with Bonferroni post hoc test was applied, considering a significance value of 5% (P < 0.05), with type I error. Results: The dentin microtensile bond strengths of preheated resin composite, flowable resin composite and dual self-adhesive cement were 6.08 ± 0.66 Mpa, 5.25 ± 2.60Mpa and 2.82 ± 1.26Mpa, respectively. In addition, the preheated resin composite exhibited significantly higher microtensile bond strength compared to the dual self-adhesive cement (P < 0.001). While the flowable resin composite showed no significant difference with the dual self-adhesive cement (P = 0.054) and the preheated resin composite (P = 0.329). Conclusions: The microtensile bond strength in dentin was significantly higher when using a preheated resin composite at 70°C as a luting agent compared to dual self-adhesive cement. However, the preheated resin composite showed similar microtensile bond strength compared to the flowable resin composite.

Tensile Strength and Elastic Modulus of Gutta-percha Cones Disinfected with Sodium Hypochlorite at Different Immersion Times: An In Vitro Comparative Study.

Aim: The tensile strength and modulus of elasticity of gutta-percha cones can be chemically altered due to disinfectant solutions. Therefore, the aim of the present study was to compare tensile strength and elastic modulus of gutta-percha cones subjected to sodium hypochlorite (NaOCl) disinfection at different times. Materials and Methods: This in vitro and longitudinal experimental study consisted of 45 gutta-percha cones, divided equally into three groups: Group 1 (disinfection with 2.5% NaOCl), Group 2 (disinfection with 5.25% NaOCl), and control group. All groups were subdivided according to immersion times for 1, 5, and 10 minutes. Tensile strength and elastic modulus were measured with a universal testing machine. For comparing more than two independent groups, parametric analysis of variance test with Sheffe's post hoc was used and for multivariate analysis, and multivariate analysis of variance test based on Pillai's Trace was used. In all statistical analysis, a significance level P ≤ 0.05 was considered. Results: When comparing the tensile strength of gutta-percha cones, no significant differences were observed after being immersed at 1, 5, and 10 minutes in NaOCl 2.5% (P = 0.715) and 5.25% (P = 0.585). Regarding the elastic modulus, a significant decrease (P < 0.05) was observed in those that were immersed in NaOCl 2.5% and 5.25% for 1, 5, and 10 minutes. Furthermore, increased NaOCl concentration significantly reduced the elastic modulus (P < 0.001). However, there were no significant differences in tensile strength (P > 0.05) and elastic modulus (P > 0.05), when evaluating the interaction between NaOCl concentration and time. Conclusion: Increasing NaOCl concentration significantly reduced the modulus of elasticity without affecting the tensile strength of gutta-percha cones, regardless of immersion time. Furthermore, the interaction of time and NaOCl concentration did not significantly affect the tensile strength and elastic modulus.

Sociodemographic Factors Associated with the Satisfaction Level of Peruvian Dental Students with Virtual Classes During the Covid-19 Pandemic: A Prospective Bicentric Study.

Background: The pandemic caused by Covid-19 impacted all areas of social, economic and educational activity. When there is a high risk of spreading highly infectious diseases, education is usually the first service to be suspended. The objective was to evaluate the sociodemographic factors associated with the satisfaction level of Peruvian dental students with virtual classes during the Covid-19 pandemic. Methods: This observational, cross-sectional, analytical study evaluated 237 dental students from the capital city and one Peruvian province using a validated 13-item questionnaire to measure the level of satisfaction with virtual classes. Pearson's chi-square test and a logit model were used to evaluate the associated factors such as age group, sex, marital status, monthly family income, area of residence, place of origin, occupation and computer use, considering a significance level of p<0.05. Results: Of all students, 50.6%, 40.1% and 9.3% presented a good, average and poor level of satisfaction, respectively, with the virtual classes received. In addition, those with a monthly family income of less than 500 US dollars were 3.15 times more likely to have poor satisfaction compared to those with a monthly family income of more than 1000 US dollars (AOR = 3.15; 95% CI: 1.23-8.05). The rest of the variables evaluated were not considered influential factors in the levels of satisfaction with the virtual classes received. Conclusión: Of all students, 50.6% and 9.3% reported good and poor satisfaction with virtual classes during the COVID-19 pandemic, respectively. Monthly family income of less than 500 US dollars was an influential factor. In addition, the variables age group, sex, marital status, area of residence, place of origin, occupation and computer use were not found to be influential factors.

Shear bond strength of three different metal bracket base designs on human premolars: An in vitro comparative study.

Background: Adequate bracket-enamel bonding is critical to prevent detachment during orthodontic treatment and minimize any potential delay in results. The aim was to compare the shear bond strength of three metal bracket base designs: laser-structured base, mesh base, and retention grooves base. Material and Methods: In this experimental in vitro study, 54 human premolars were immersed for one week in 0.1% thymol solution, then placed in distilled water with weekly replacement until the start of the study. The premolars were cemented with brackets of varying base designs: A. Discovery® Smart (laser structured), B. Mini Master® Series (base with mesh), and C. Roth Max (base with retention grooves). All brackets were cemented using TransbondTM XT. A universal testing machine was used to evaluate the shear bond strength at a crosshead speed of 0.75 mm/min. Welch's one-factor ANOVA with robust variance and Tukey's post hoc test were used to compare means, with a significance level of p<0.05. Results: The average shear bond strength values were for the bracket with laser-structured base (14.78 ± 5.79 MPa), the bracket with mesh base (9.64 MPa ± 2.54 MPa) and the bracket with retention groove base (15.38 MPa ± 2.67 MPa). It was found that brackets with mesh bases had significantly lower shear bond strength than brackets with laser-structured bases (p=0.001) and brackets with retention grooves bases (p<0.001). No significant differences were observed between the latter two types of brackets (p = 0.893). Conclusions: The bracket base design influenced in vitro shear bond strength with significantly higher values observed for Roth Max and Discovery® Smart brackets compared to Mini Master® Series brackets. Key words:Shear strength, laser-structured bracket, bracket with mesh base, bracket with retention groove base.

Impact of an Educational Intervention on Oral Health Knowledge and Bacterial Plaque Control in Male Secondary School Students in a Peruvian Province: A Quasi-Experimental Study.

Background: The purpose of this study was to evaluate the effect of an educational intervention on oral health knowledge and bacterial plaque control in male secondary school students in a Peruvian province. Methods: This quasi-experimental study evaluated 294 male secondary school students in southern Peru. Oral health knowledge was measured with a validated 20-item questionnaire. Bacterial plaque was measured with the Simplified Oral Hygiene Index (OHI-S). This was rated as Excellent: 0, Good: 0.1-1.2, Fair: 1.3-3.0 and Poor: 3.1-6.0, before receiving the educational intervention and after four weeks of receiving it. Variables such as age, area of residence, having health professionals as family members, educational level of mother and father, and living with parents were considered. A significance level of p<0.05 was considered. Results: The comparison between the level of oral health knowledge and the OHI-S, before and after 4 weeks of receiving the educational intervention, showed a significant improvement (p<0.05) in all the categories of the variables studied. Likewise, before the educational intervention, there were significant differences in global knowledge about oral health among the categories of the following variables: age group (p=0.040), area of residence (p<0.001), educational level (father) (p=0.011) and living with parents (p<0.001). However, after four weeks of receiving the educational intervention, no significant differences were observed in all the variables studied (p>0.05). Regarding the OHI-S, no significant differences were observed in any of the variables studied, both before (p>0.05) and after four weeks (p>0.05) of receiving the educational intervention. Conclusion: After four weeks, the educational intervention significantly improved oral health knowledge and significantly reduced plaque bacterial plaque in male secondary school students in a Peruvian province, regardless of age, area of residence, having health professional family members, educational level of mother and father, and living with parents.

Sociodemographic factors associated with knowledge and attitudes of Peruvian dental interns about dental shade selection.

BACKGROUND: The dentist should have a thorough knowledge of the science, protocols and procedures for dental shade selection in order to mimic dental tissue with restorative materials, respecting the individual needs and attitudes of each patient and providing them with a pleasant and esthetically acceptable appearance. The present study evaluated the knowledge and attitudes of dental interns from two Peruvian universities about dental shade selection and its relationship with sociodemographic factors. METHODS: The present cross-sectional and analytical study was carried out on Peruvian dental interns from the Universidad Nacional Federico Villarreal and the Universidad Privada de San Juan Bautista during May to June 2022. Two validated questionnaires on knowledge and attitudes about dental shade selection were used. A Poisson regression model with robust variance using the adjusted prevalence ratio (APR) was used to assess the influence of the variables: age group, sex, place of origin and type of university, considering a significance level of p<0.05. RESULTS: The results showed that 40.8% (95% CI: 34.0% - 47.6%) of the interns presented unfavorable attitudes while 90.1% (95% CI: 86.0% - 94.2%) presented insufficient knowledge. It was also found that dental interns under 29 years of age were 32% less likely to have unfavorable attitudes (APR = 0.68, 95% CI 0.48 - 0.96) and 11% more likely to have insufficient knowledge (APR = 1.11, 95% CI 1.01 - 1.24) about tooth shade selection compared to dental interns aged 29 years and older. Finally, women were 55% more likely to have unfavorable attitudes about tooth shade selection compared to men (APR = 1.55; 95% CI: 1.08 - 2.22). CONCLUSION: The majority of dental interns presented insufficient knowledge and less than half had unfavorable attitudes about dental shade selection. In addition, being a student under 29 years of age was a risk factor for presenting insufficient knowledge and at the same time constituted a protective factor for presenting unfavorable attitudes. Likewise, being a female student was a risk factor for presenting unfavorable attitudes about dental shade selection.

Resonance Frequency Analysis Mapping During Implant Healing Using a Nanostructured Hydroxyapatite Surface.

Aim: Stability measured by resonance frequency analysis (RFA) is an important factor to be considered in the success of dental implant treatments, which can be evaluated from the implant stability quotient (ISQ). The aim of the present case series was to map the RFA during healing of implants with nanostructured hydroxyapatite surface to describe the behavior of ISQ values related to individual factors. Materials and Methods: Twenty-three implants were placed in eight patients by conventional surgical protocol, and ISQ values were monitored from the day of implant placement until week 20. To obtain the ISQ values, an Osstell device was used and the placed implants were grouped in proportional amounts to describe the ISQ behavior considering the length (≤10 or >10 mm), the diameter (3.5 or 4.3 mm), the insertion torque (<40 N-cm or ≥40 N-cm), and the placement area (maxilla or mandible). Results: All the implants assessed decreased their values in the first 3 weeks after placement. Subsequently, the ISQ values increased by amounts similar to those obtained at the time of the placement and even more. Implants with length >10 mm, diameter 4.3 mm, and insertion torque ≥40 N-cm showed the highest ISQ values. Conclusions: A decrease in the ISQ values of dental implants with nanostructured hydroxyapatite surface was evidenced between weeks 2 and 3 considering length, diameter, insertion torque, and maxillary or mandibular placement site.

Sociodemographic Factors Associated with Knowledge About Management of Cleft Lip and Palate Patients in Peruvian Dental Students: A Logistic Regression Analysis.

Background: Cleft lip and palate are relatively frequent craniofacial alterations caused by the lack of union of the frontonasal processes with the maxillary processes during the first weeks of intrauterine life. This study evaluated the sociodemographic factors associated with the level of knowledge about management of cleft lip and palate (CLP) patients in Peruvian dental students. Methods: This analytical, observational, cross-sectional and prospective study evaluated 191 dental students belonging to two branches of a private Peruvian university (one branch in the capital city and the other in a province), from September to November 2022. A validated questionnaire of 14 closed multiple-choice questions was used. A logit model was used to evaluate the influence of the variables: sex, age, academic year of study, marital status, relationship with CLP persons, place of origin and area of residence, on the level of knowledge of the students considering a significance level of p<0.05. Results: Of the total, 77%, 22.5% and 0.5% presented a poor, fair and good level of knowledge, respectively, on the dental management of the patient with cleft lip and palate. In addition, those who lived in urban areas were 2.8 times more likely to have poor knowledge about the dental management of patients with CLP, compared to those who lived in non-urban areas (OR = 2.83; 95% CI: 1.26-6.33). Finally, sex, age, marital status, place of origin, academic year of studies and relationship with CLP persons were not considered influential factors (p>0.05). Conclusion: Most of the students showed a poor level of knowledge about the dental management of patients with cleft lip and palate, a risk factor being that the students live in an urban area. It is recommended that educational authorities include selected topics on CLP in subjects related to infant, child and adolescent care.

Microleakage in indirect onlay restorations cemented with three different types of adhesives: An in vitro study.

Background: To evaluate the in vitro degree of marginal microleakage in indirect Class II onlay restorations cemented with dual self-adhesive, universal adhesive and dual adhesive. Material and Methods: In the present in vitro experimental study, a total of 54 human premolar teeth were prepared and divided into three equal groups (n = 18) for placement of onlay-type restorations cemented with A: Allcem™ dual-cure adhesive cement), B: RelyX™U200 dual-cure self-adhesive cement and C: RelyX™ Ultimate universal adhesive cement. All restorations were subjected to 10,000 thermocycles between 5°C and 55°C and immersed in a 1M silver nitrate solution for 6 hours. The crowns were then sectioned mesiodistally and observed under a stereo microscope to determine the degree of marginal microleakage in the cervical area. Results: The onlay restorations cemented with RelyX Ultimate did not present microleakage in the majority of cases (77.8%). Restorations cemented with RelyX U200 showed predominantly microleakage up to the pulp floor in 83.3% of the total, being this significantly higher microleakage than in restorations cemented with RelyX Ultimate and Allcem Dual (p<0.001 and p<0.001 respectively). There was no significant difference in microleakage between the last two mentioned cements (p=0.255). Conclusions: Allcem dual adhesive cement and RelyX Ultimate universal adhesive showed significantly less microleakage than RelyX U200 dual-curing self-adhesive cement at the cervical level, with predominantly no microleakage and microleakage down to the enamel, respectively. The use of RelyX Ultimate cement in indirect restorations is recommended as it showed better marginal adaptation. Key words:Microleakage, human teeth, adhesion, adhesive cement, thermal cycling, onlay restoration.

Factors Associated with the Level of Knowledge about Biosafety against COVID-19 in Peruvian Dental Students: A Cross-Sectional Study under a Multivariable Regression Model.

AIM: Biosafety is a set of preventive measures aimed at controlling risk factors arising from biological, physical, and/or chemical agents. This topic is particularly important in the dental field since saliva is the main biological agent of the transmission of coronavirus. The present study aimed to determine the factors associated with the level of knowledge about biosafety against COVID-19 in Peruvian dentistry students. MATERIALS AND METHODS: The present observational, cross-sectional, and analytical study evaluated 312 Peruvian dentistry students. A validated 20-question questionnaire was used to measure the level of knowledge. The nonparametric Mann-Whitney U and Kruskal-Wallis tests were used to compare levels of knowledge between categories of each variable. A logit model was used to evaluate associated factors such as sex, age, marital status, place of origin, academic year of study, being in the academic upper third, history of COVID-19, and living with vulnerable family members. A significance level of p < 0.05 was considered. RESULTS: 36.2%, 31.4%, and 32.4% presented poor, fair, and good knowledge levels, respectively. Students under 25 years of age were 64% less likely to pass the biosafety against COVID-19 questionnaire than students 25 years of age and older (OR = 0.36; CI: 0.20-0.66). Students in the academic upper third were nine times more likely to pass the test than other students (OR = 9.38; CI: 4.61-19.07). Finally, third-year students were 52% less likely to pass the exam than fifth-year students (OR = 0.48; CI: 0.28-0.83). CONCLUSION: Only a minority of dentistry students had a good level of knowledge about biosafety against COVID-19. Younger and less educated students were more likely to fail the questionnaire. On the other hand, those students with outstanding academic performance were more likely to pass the questionnaire.

Factors associated with the perception of university professors about academic dishonesty in dental students from two peruvian universities: analysis under multivariable regression model.

BACKGROUND: Academic dishonesty is an intentional behavior that transgresses ethics in the teaching-learning process. The present study aimed to evaluate the factors associated with the perception of university professors about academic dishonesty in dental students from two universities in the Peruvian capital. METHODS: This cross-sectional, analytical study evaluated 181 professors from two Peruvian universities between March and July 2022. A validated 28-item questionnaire was used to measure the perceived academic dishonesty of their students. A logit model was used to evaluate the influence of the variables gender, marital status, place of origin, academic degree, specialization, academic area, years of teaching experience, scientific publications, ethical training and university of origin, considering a significance level of p < 0.05. RESULTS: According to the median, professors perceived that their students sometimes had attitudes and motivations to commit academic dishonesty. The professors whose origin was the capital city were twice as likely to perceive dishonest attitudes in dental students as those whose origin was a province (OR = 2.04; 95% CI: 1.06-3.93). University professors in pre-clinical courses were 0.37 times less likely to perceive dishonest attitudes than those teaching in the dental clinic (OR = 0.37; CI: 0.15-0.91). University professors in basic science courses and professors in preclinical courses were 0.43 times (OR = 0.43; CI: 0.19-0.96) and 0.39 times (OR = 0.39; CI: 0.15-0.98) less likely to perceive dishonest motivations in their students compared to university professors in the dental clinic. Gender, marital status, academic degree, specialty, years of teaching experience, scientific publications and ethical training were not found to be influential factors (p > 0.05). CONCLUSION: Although all university professors surveyed perceived dishonest attitudes and motivations in their students, university professors from the capital city perceived such attitudes more. In addition, being a preclinical university professor was a hindered factor for perceiving such dishonest attitudes and motivations. It is advisable to implement and constantly disseminate regulations that empower academic integrity as well as to manage a system for reporting misconduct and to make students aware of the impact of dishonesty in their professional training.

Bond Strength and Failure Mode of Glass Fiber Posts with Different Surface Treatments Prior to Silanization: An In Vitro Comparative Study.

Aim: The use of chemical agents in the surface treatment of glass fiber posts can improve their bond strength to the root canal. The aim of this study was to assess the bond strength and failure mode of glass fiber posts that received different surface treatments prior to silanization. Materials and Methods: In this cross-sectional and in vitro experimental study, 50 human lower premolar roots were randomly divided into five groups and subsequently prepared to receive the cementation of a fiberglass post prior to silanization. They were distributed as group 1 (with 24% hydrogen peroxide), group 2 (with 37% phosphoric acid), group 3 (with 1.23% acidulated phosphate fluoride for 2 minutes), group 4 (with 1.23% acidulated phosphate fluoride for 6 minutes), and group 5 (without pretreatment). After cementation, the roots were sectioned into two discs for each cervical, middle, and apical region. Bond strength was assessed using the push out technique. Adhesive, mixed, and cohesive failure modes were also assessed. For data analysis, ANOVA and Tukey's post hoc tests were used, as well as Pearson's chi-square test. A significance of P < 0.05 was considered in all statistical analyses. Results: When comparing the bond strength of root regions, significant differences were obtained in groups pretreated with phosphoric acid (P = 0.018) and acidulated phosphate fluoride for 2 and 6 minutes (P = 0.001 and P = 0.000, respectively). Furthermore, significant differences were obtained between posts treated only with silane and those that received phosphoric acid pretreatment (P = 0.006) and acidulated phosphate fluoride for 6 minutes (P = 0.001). Significant association of mixed failure mode was observed with hydrogen peroxide (P = 0.014) and phosphoric acid (P = 0.006) pretreatments. Cohesive failure was significantly associated with acidulated phosphate fluoride pretreatment for 2 minutes (P = 0.032) and with posts that did not receive treatment prior to silanization (P = 0.000). Conclusion: Posts treated only with silane and pretreated with hydrogen peroxide and acidulated phosphate fluoride for 2 minutes presented significantly higher bond strength with respect to those pretreated with phosphoric acid and acidulated phosphate fluoride for 6 minutes. However, acidulated phosphate fluoride for 2 minutes and silane were associated with a better bonding type.

Surface Roughness in Nanoparticle Resin Composites Subjected to Two Polishing Systems: An In vitro Comparative Study.

Aim: The surface roughness of dental restorations can decrease resin durability, since it leads to its deterioration, color variation, and loss of gloss. Therefore, the aim was to assess the surface roughness of nanoparticle resin composites, subjected to two different polishing systems. Materials and Methods: This longitudinal in vitro experimental study consisted of 32 resin specimens made according to ISO 4049-2019 and divided equally into four groups: A1: Palfique LX5 / Sof-Lex, A2: Palfique LX5 / Super Snap, B1: Filtek Z350 XT / Sof-Lex, and B2: Filtek Z350 XT / Super Snap. The samples were stored in distilled water at 37°C for 24 h. Surface roughness was measured with a digital roughness tester, both before and after the polishing procedure. The data were analyzed with the Student's t-test for related samples, and with the inter-subject ANOVA test with two factors; considering significance at P < 0.05. Results: The surface roughness of Palfique LX5 resin with the Sof-lex system was 0.330 (CI: 0.282-0.378 µm) and 0.170 (CI: 0.087-0.253 µm) before and after polishing, respectively. With the Super Snap system, values of 0.448 (CI: 0.346-0.549 µm) and 0.206 (CI: 0.130-0.282 µm) were obtained before and after polishing, respectively. For the Filtek Z350 XT resin, the surface roughness obtained with the Sof-lex system was 0.353 (CI: 0.278-0.427 µm) and 0.134 (CI: 0.095-0.172 µm) before and after polishing, respectively. With the Super Snap system, values of 0.334 (CI: 0.247-0.421 µm) and 0.171 (CI: 0.122-0.221 µm) were obtained before and after polishing, respectively. Surface roughness did not show significant differences in all groups assessed both before (P = 0.068) and after (P = 0.335) polishing. However, before and after the application of the polishing systems, all groups significantly decreased their surface roughness (P < 0.05). Further, when comparing this decrease among all groups, no significant differences were observed (P = 0.437). Conclusion: The surface roughness of the Filtek Z350 XT and Palfique LX5 nanoparticle resin composites showed no significant differences when using the Sof-lex and Super Snap polishing systems. However, both polishing systems significantly decreased the surface roughness of the nanoparticulated resins, with this decrease being similar in all groups.

In Vitro Color Stability Evaluation of Three Polished and Unpolished Nanohybrid Resin Composites Immersed in a 0.12% Chlorhexidine-Based Mouthwash at Different Times.

The use of chlorhexidine-based mouthwashes on resin composites with rough surfaces can cause discoloration which compromises the esthetic of patients. The present study aimed to evaluate the in vitro color stability of Forma (Ultradent Products, Inc., South Jordan), Tetric N-Ceram (Ivoclar Vivadent, Schaan, Liechtenstein) and Filtek Z350XT (3M, ESPE, St. Paul, MN, USA) resin composites, with and without polishing, after being immersed in a 0.12% chlorhexidine (CHX)-based mouthwash at different times. The present in vitro experimental and longitudinal study used 96 nanohybrid resin composite blocks (Forma, Tetric N-Ceram and Filtek Z350XT) 8 mm in diameter and 2 mm thick, evenly distributed. Each resin composite group was divided into two subgroups (n = 16) with and without polishing and then immersed in a 0.12% CHX-based mouthwash for 7, 14, 21 and 28 days. Color measurements were performed with a calibrated digital spectrophotometer. Nonparametric tests were used to compare independent (Mann-Whitney U and Kruskal-Wallis) and related (Friedman) measures. In addition, the Bonferroni post hoc correction was used considering a significance level of p < 0.05. All polished and unpolished resin composites presented color variation < 3.3 when immersed for up to 14 days in 0.12% CHX-based mouthwash. The polished resin composite with the lowest color variation (ΔE) values over time was Forma, and the one with the highest values was Tetric N-Ceram. When comparing the color variation (ΔE) over time, it was observed that the three resin composites, with and without polishing, presented a significant change (p < 0.001), although these changes in color variation (ΔE) were evident from 14 days between each color acquisition (p < 0.05). The unpolished Forma and Filtek Z350XT resin composites showed significantly more color variation than the same polished ones at all times when immersed in a 0.12% CHX-based mouthwash for 30 s daily. In addition, every 14 days, all three resin composites with and without polishing showed a significant color change, while, every 7 days, color stability was maintained. All the resin composites showed clinically acceptable color stability when exposed for up to 14 days to the above-mentioned mouthwash.

Factors associated with knowledge about pharmacological management of pregnant women in Peruvian dental students: a logistic regression analysis.

BACKGROUND: Clinical management to maintain or restore oral health through the use of drugs during pregnancy is crucial, since at this stage physiological changes significantly influence the absorption, distribution and elimination of the drug, considering also that excessive administration of drugs during this period may have adverse effects on the mother and/or fetus. Therefore, the aim of the present study was to evaluate the factors associated with knowledge of pharmacological management of pregnant women in dental students of a Peruvian university located in the capital and province. METHODS: This analytical, cross-sectional, prospective and observational study assessed 312 Peruvian dental students from third to fifth year of study between February and April 2022. A validated questionnaire of 10 closed questions was used to measure knowledge about pharmacological management in pregnant women. A logit model was used to assess the influence of the variables: gender, age, year of study, marital status, place of origin and area of residence. A significance of p < 0.05 was considered. RESULTS: The 25.96, 55.13 and 18.91% of the dental students showed poor, fair and good knowledge about pharmacological management in pregnant women; respectively. In addition, it was observed that students under 24 years of age and those from the capital were significantly (p < 0.05) 44% less likely to have poor knowledge of pharmacological management in pregnant women compared to those aged 24 years or older (OR = 0.56; CI: 0.34-0.92) and those from the province (OR = 0.56; CI: 0.32-0.98); respectively. Finally, those in their third and fourth year of study were significantly three times more likely to have poor knowledge (OR = 3.17; CI: 1.68-5.97 and OR = 3.88; CI: 2.07-7.31; respectively) compared to fifth year dental students. CONCLUSION: The knowledge of dental students about pharmacological management in pregnant women was predominantly of fair level. In addition, it was observed that being under 24 years of age and being from the capital city were protective factors against poor knowledge, while being a third- and fourth-year student was a risk factor. Finally, gender, marital status and area of residence were not influential factors in the level of knowledge.

Microleakage of Class II Bulk-Fill Resin Composite Restorations Cured with Light-Emitting Diode versus Quartz Tungsten-Halogen Light: An In Vitro Study in Human Teeth.

Background: Resin composites undergo a certain degree of shrinkage when light-cured with different light sources available on the market, resulting in microleakage of dental restorations. The aim of the present study was to assess microleakage of class II restorations with bulk-fill resin composites cured with LED (light-emitting diode) and QTH (quartz tungsten-halogen light) units, both in cervical and occlusal areas of cavity preparations. Materials and Methods: In the present in vitro experimental study, a total of 30 human molar teeth were used, in which 60 class II cavities were prepared (mesial and distal) and restored with Filtek bulk fill resin composite. Restorations were equally distributed in 3 groups according to type of curing light: A, QTH (Litex 680A Dentamerica®); B, LED (Bluephase N® 3rd generation); and C, LED (Valo® 3rd generation). Each group was further subdivided into subgroups 1 and 2 according to IV-A or IV-B resin composite color. Restored teeth were subjected to 20,000 thermal cycles between 5° and 55 °C, then immersed in 1M silver nitrate solution for 24 h. Subsequently, the teeth were sectioned mesiodistally to obtain samples for observation under stereomicroscope in order to determine microleakage degree. Kruskal-Wallis H and Mann-Whitney U statistical tests were applied with a significance level of 5% (p < 0.05). Results: No statistically significant differences were found in the degree of microleakage of bulk-fill resin composites light-cured with LED and QTH units for both occlusal (p > 0.05) and cervical areas (p > 0.05). Additionally, no significant differences were found when comparing microleakage between occlusal and cervical areas (p > 0.05), regardless of lamp type. In addition, significant differences in microleakage degree were found between bulk-fill resins with IV-A and IV-B shades when they were light-cured with QTH at cervical level (p = 0.023). However, there were no significant differences when comparing these bulk-fill resin composite shades at occlusal level with LED (p > 0.05) and QTH (p > 0.05) units. Conclusions: Class II restorations with bulk-fill resin composite in IV-A and IV-B shades light-cured with third generation LED lamp and QTH showed no significant differences in microleakage when compared in both occlusal and cervical areas. On the other hand, significantly more microleakage was found at the cervical level when a darker shade of resin composite was used and light-cured with the QTH unit.

Sociodemographic Factors Associated with the Level of Knowledge of Early Postpartum Women about Oral Health Prevention in Infants Aged 0 to 2 Years Old: A Cross-Sectional Study under a Multivariable Analysis.

The objective was to evaluate the sociodemographic factors associated with the level of knowledge of early puerperal women about oral health prevention in infants. This cross-sectional and analytical study evaluated 303 early puerperal women from a hospital in the Peruvian capital. A validated 18-question questionnaire was used to measure the level of knowledge. A logistic regression model was used to evaluate the influence of age, marital status, educational level, number of children, monthly income, and having a dentist as a family member. A significance of p < 0.05 was considered. A total of 46.86%, 30.36%, and 22.77% of the puerperal had poor, fair, and good knowledge, respectively. The risk of having poor knowledge was two times higher (OR = 2.43; CI: 1.26-4.70) in early postpartum women aged 18 to 25 years than in those older than 35 years. Early postpartum women with no education, primary and secondary education were 11 times (OR = 11.76; CI: 2.41-57.43), 6 times (OR = 6.61; CI: 1.72-25.45), and 5 times (OR = 5.50; CI: 1.52-19.89), respectively, more likely to have significantly poor knowledge compared to those with university education. In conclusion, only a small minority of early postpartum women had a good knowledge of oral health prevention in infants aged 0 to 2 years. Younger and less educated puerperal were at greater risk of having little knowledge on this topic. Finally, not having basic education was the main risk factor identified.

Sociodemographic factors associated with the level of knowledge about management of epileptic patients in Peruvian dental students: a cross-sectional study under a multivariable analysis.

BACKGROUND: Epilepsy is a chronic neurological disease that could indirectly affect oral health, and it is necessary for dentists to be familiar with the specific needs of patients with epilepsy. Therefore, aim of the present study was to assess the factors associated with the level of knowledge about management of epileptic patients in Peruvian dental students. METHODS: This analytical, observational, cross-sectional and prospective study assessed 312 dental students from a Peruvian university during February to April 2022. A validated questionnaire of 20 closed multiple-choice questions was used to measure the level of knowledge about dental management in epileptic patients. A logit model was used to assess the influence of variables: gender, age, year of study, marital status, place of origin and area of residence, with the level of knowledge in dental students considering a significance level of p < 0.05. RESULTS: Of the total, 28.8%, 36.2% and 34.9% had a poor, fair and good level of knowledge, respectively, about the dental treatment of epileptic patients. On the other hand, it was observed that being a woman (OR = 0.44, CI 0.26-0.75) and being a third year student (OR = 0.39, CI 0.21-0.74) and fourth year student (OR = 0.43, CI 0.23-0.89) constituted a protective factor against poor knowledge about the dental management of epileptic patients, while being from the capital city constituted a risk factor. Finally, age, marital status and the students' area of residence were not considered influential factors (p > 0.05). CONCLUSION: Most of the students showed a poor and fair level of knowledge about the dental management of epileptic patients, with gender, academic year and place of origin being influential factors. It is advisable that authorities and teachers in the dental profession organize recurrent training programs on the care of patients with chronic diseases requiring special attention, since knowing general concepts, pharmacological management and dental care of epileptic patients will allow future dentists to develop competencies to improve and implement good quality care protocols for this group of patients.

Factors Associated with Epidemiological, Preventive and Health Care Knowledge of Dentists from North of the Peruvian Capital about COVID-19: A Cross-Sectional Study under a Predictive Model.

Aim: In dental practice there is a high risk of contact with fluids that may contain SARS-CoV-2. Salivary secretions in the form of droplets are the main route of infection. The present study aimed to evaluate factors associated with epidemiological, preventive and health care knowledge of dentists from the north of the Peruvian capital about COVID-19. Materials and Methods: This analytical, observational, cross-sectional and prospective study evaluated 142 dental professionals from the Directorate of Integrated Health Networks (DIRIS) in the north of the Peruvian capital during June to August 2022. A validated questionnaire of 20 closed multiple-choice questions was used to measure the level of epidemiological, preventive and health care knowledge about COVID-19. A logit model was used to evaluate the influence of the following variables: age, sex, marital status, children, origin, university of origin, academic degree, work modality, work status and number of training courses. In addition, a predictive model was constructed with the causal variables considering a significance level of p < 0.05. Results: Epidemiological, preventive and health care knowledge about COVID-19 was fair in 17.6%, 34.5% and 57.7%, respectively. Likewise, all the variables analyzed were influential factors. It was observed that being single (OR = 0.05, CI: 0.01−0.26), having studied at a private university (OR = 0.09, CI: 0.023−0.38) and having received four to six trainings on COVID-19 related topics (OR = 0.02, CI: 0.002−0.238) were protective factors against fair knowledge. Conclusions: More than half of the dentists surveyed had fair knowledge about COVID-19. The factors that favored a good level of overall knowledge were: being single, having studied at a private university and having received 4 to 6 training courses on COVID-19-related topics. It is advisable that the competent authorities continue to educate dental professionals with training programs about infection control practices in accordance with the health care work they perform in their specialty. It will also be of utmost importance for the professional to be updated with reliable information accredited by the Centers for Disease Control and Prevention as well as the WHO.

Surface Microhardness of Bulk-Fill Resin Composites Handled With Gloves.

AIM: It has been reported that resin composites may experience alterations in their mechanical properties when they come into contact with glove powder. Therefore, the present study aimed to compare the surface microhardness of 3 bulk-fill resin composites handled with latex and nitrile gloves prior to light curing. METHODS: This in vitro experimental study consisted of 90 resin composite specimens with a 6-mm diameter and a 4-mm height divided equally and randomly into 9 groups. Prior to light curing, the resin composites were handled with latex gloves, nitrile gloves, or only a spatula (control). Subsequently, the surface microhardness was measured with an Electronic Vickers Hardness Tester. The Kruskal-Wallis nonparametric H test with Bonferroni correction was used for comparisons. A significance level of 5% (P < .05) was considered. RESULTS: When comparing surface microhardness of each resin composite according to type of handling received, significant differences were observed in Filtek One Bulk Fill (P < .001) and Opus Bulk Fill (P < .001). In addition, these resin composites presented significantly higher surface microhardness than Tetric N-Ceram Bulk Fill resin (P < .05) when handled with latex gloves, nitrile gloves, and only a spatula. Finally, Filtek Bulk Fill resin presented significantly higher surface microhardness compared to Opus Bulk Fill resin when handled with nitrile gloves (P = .038) and a spatula only (P = .033). CONCLUSIONS: The surface microhardness of Filtek One Bulk Fill and Opus Bulk Fill resin composites decreased significantly when handled with latex or nitrile gloves, showing no variation in Tetric N-Ceram Bulk Fill resin composite. In addition, Filtek One Bulk Fill resin composite showed significantly higher surface microhardness than Opus Bulk Fill and Tetric N-Ceram Bulk Fill resin composites when handled with nitrile gloves. It is recommended that bulk-fill resin composites be handled with a spatula, because the use of latex or nitrile gloves could adversely affect their clinical performance.